                        Chlorinated Polyethylene Resin

                        As an excellent impact modifier, Keliren? chlorinated polyethylene thermoplastic resin is widely used in PVC extrusion and injection molding products, including profiles, pipes, sheets and fittings. The addition of a small amount of Keliren? resin can greatly enhance the impact resistance of rigid PVC and improve its processing fluidity. In addition, due to its good chemical resistance, outstanding low-temperature performance, high filling capacity, excellent weather resistance and remarkable compatibility, Keliren? resin is used in a wider range of formulation systems.

                        Application fields

                        • CPE is currently the most widely used and most economical impact modifier in the PVC profile industry.

                        • Keliren? resin is able to improve the impact resistance and aging properties of PVC pipes significantly. CPE is especially widely used in large-diameter pressure-resistant liquid conveying pipes to improve its pressure bearing performance and extend its service life.

                        • When Keliren? resin is blended with PVC to produce soft products, CPE acts as a permanent polymer plasticizer for PVC to avoid the migration of general plasticizers (such as DOP) .

                        • Keliren? resin is also used as a modifier and compatibilizer in flame retardant ABS, SAN, HDPE and PP materials to improve their impact resistance and flame retardancy.

                        • Keliren? resin is also used in the sole industry due to its good wear resistance and flex resistance.

                        Modified chlorinated polyethylene (I) Technical indexes

                        No.

                        Item

                        		UnitCPE132CCPE1135CCPE135CCPE235CTest method
                        1Chlorine contentwt%32±135±135±135±1GB/T9872
                        2Shore hardnessShore A≤60≤57≤57≤60GB/T531
                        3Tensile strength MPa≥8.0≥8.5≥8.5≥8.5GB/528
                        4Elongation at break%≥800≥800≥800≥800GB/528
                        5Application-FR-ABS,Flexible PVC FR-ABS,Flexible PVC PE film   FR-ABS,Flexible PVC PE film  FR-ABS Impact modifier -
                        6Performance-


                        Low residual crystalline and good

                        processing flowability

                        Low residual crystalline and good 

                        processing flowability

                        Low residual crystalline and good 

                        processing flowability

                        Moderate residual crystalline, 

                        can be stored in silo

                        		-

                        Modified chlorinated polyethylene (II) Technical indexes

                        No.ItemUnit CPE142CCPE6325CPE3610CPE3605Test method
                        1Chlorine contentwt%40±136±136±136±1GB/T9872
                        2Shore hardnessShore A≤65≤60≤60≤60GB/T531
                        3Tensile strength MPa≥8.0≥8.5≥8.5≥8.5GB/528
                        4Elongation at break%-≥600≥600≥600GB/528
                        5Application-

                        FR-ABS, PE film 

                        Impact modifier

                        used in high-speed extrusion PVC products


                        		Impact modifier, used in high-speed  extrusion PVC productsImpact modifier,used in PVC products-
                        6Performance-Good processing flowability and outstanding flame resistance 

                        Excellent processing flowability

                        		Much outstanding processing flowability

                        Good processing flowability and Good impact modification performance

                        		-
                        Return